Copertina di Improving thermal & mechanical properties for bentonite ceramic's body
Titolo del libro:

Improving thermal & mechanical properties for bentonite ceramic's body

Bentonie ceramic's body

LAP LAMBERT Academic Publishing (02.11.2012 )

Books loader

Omni badge eleggibile a buono
ISBN-13:

978-3-659-29309-2

ISBN-10:
3659293091
EAN:
9783659293092
Lingua del libro:
Inglese
Risvolto di copertina:
The most important achieved results in the research are: First Al-Safra activated clay by using sodium carbonate at ratio wt% (5%) with the additives (alumina and magnesia) underwent firing temperature at(1300 ºC) without any distortion in the appearance and gave the maximum compressive strength to (60.41 MPa), which is higher than of the bentonite (as a based material, of about 8.47 MPa). Second: Qara Tappah activated bentonite by using ratios of Na2CO3 at (5% and 7.5%) showed an undergoing to the heat treatment to 1400 ºC without any distortion and shrinkage in dimensions and best value of the thermal conductivity as a thermal insulator which was (0.039 W/m.K).
Casa editrice:
LAP LAMBERT Academic Publishing
Sito Web:
https://www.lap-publishing.com/
Da (autore):
Entesar Abbas Hamed Al-Ethawei, Fadhil A.Rasin
Numero di pagine:
128
Pubblicato il:
02.11.2012
Giacenza di magazzino:
Disponibile
categoria:
Altro
Prezzo:
59,00 €
Parole chiave:
Alumina, Magnesia, Bentonite Clay

Books loader

Newsletter

Adyen::diners Adyen::jcb Adyen::discover Adyen::amex Adyen::mc Adyen::visa Adyen::cup Adyen::unionpay Adyen::paypal Paypal CryptoWallet Trasferimento

  0 prodotti nel carro d'acquisti
Modificare il carrello
Loading frontend
LOADING